Size Matters When Reducing NiO Nanoparticles
November 26th, 2012
New research finds that size plays a major role in how nanoscale nickel oxide (NiO) shells behave when being reduced to solid nickel nanoparticles.
“This advances our fundamental understanding of how the structures of nanoparticles can be changed through chemical reactions, which has potential applications in nanofabrication and catalysis," says Joe Tracy, a materials scientist at NC State and co-author of a paper on the work.
The researchers began by exposing nickel nanoparticles to air at 500 degrees Celsius in order to create NiO shells. This process is called oxidation. The smaller shells, 12 to 24 nanometers (nm) in diameter, are hollow, with the shell surrounding a single cavity. Larger shells, 40 to 96 nm in diameter, appear to have larger pores, and possibly contain multiple cavities.
The researchers then placed the shells in a hydrogen gas environment at 350 degrees C. This process, called reduction, turns the NiO shells back into solid nickel nanoparticles.
What they found was that the size of the NiO shells dramatically affects the way that the reduction process manifests itself.
The smallest shells the researchers looked at, 12 nm in diameter, formed a single nucleation site of pure nickel, which then expanded to replace all of the NiO. Larger shells, 24 nm in diameter, responded differently - forming multiple nucleation sites in an approximate ring shape around the shell. These nucleation sites then grew and merged into a single nickel nanoparticle. The largest shells they looked at, 96 nm in diameter, looked more different still, with multiple nucleation sites forming throughout the NiO.
“The size of the nanoparticles before oxidation determines both the structure of the NiO nanoparticles and the pattern of the nucleation sites of nickel metal during reduction,” says John Medford, an undergrad at NC State and lead author of the paper.
The paper, “Nanostructural Transformations During the Reduction of Hollow and Porous Nickel Oxide Nanoparticles,” was published online Nov. 20 in the Royal Society of Chemistry journalNanoscale. The paper was co-authored by Aaron Johnston-Peck, of Brookhaven National Laboratory. The research was supported by the National Science Foundation, U.S. Department of Education, North Carolina State University and Protochips, Inc.
Other Recent News
- MSE Wins Multiple Awards and Provides Leadership at Microscopy and Microanalysis 2017 8.14.2017
- High-Temperature Superconductivity in B-doped Q-Carbon 7.24.2017
- IRES Students Gain Research experience in Denmark 7.21.2017
- MSE Graduate Student Wins MRS Poster Award 5.23.2017
- ‘Persistent Photoconductivity’ Offers New Tool for Bioelectronics 5.3.2017
- Eman Alhajji accepted into NAE Grand Challenge Scholars Program 5.2.2017
- MSE Undergrad and Grad Named Recipients of NSF’s Graduate Research Fellowship 4.28.2017
- Silicon Valley Favors NC State Alumni 4.27.2017
- Thin Layers of Water Hold Promise for the Energy Storage of the Future 4.27.2017
- From Atoms to Batteries to the Workforce of the Future: Why Research Matters 4.25.2017