High-Temperature Superconductivity in B-doped Q-Carbon
July 24th, 2017
Researchers at North Carolina State University have significantly increased the temperature at which carbon-based materials act as superconductors, using a novel, boron-doped Q-carbon material.
The previous record for superconductivity in boron-doped diamond was 11 Kelvin, or minus 439.60 degrees Fahrenheit. The boron-doped Q-carbon has been found to be superconductive from 37K to 57K, which is minus 356.80 degrees F.
“Going from 11K to 57K is a big jump for conventional BCS superconductivity," says Jay Narayan, the John C. Fan Distinguished Chair Professor of Materials Science and Engineering at NC State and senior author of two papers describing the work. BCS refers to the Bardeen-Cooper-Schrieffer theory of superconductivity.
Regular conductive materials conduct electricity, but a lot of that energy is lost during transmission. Superconductors can handle much higher currents per square centimeter and lose virtually no energy through transmission. However, superconductors only have these desirable properties at low temperatures. Identifying ways to achieve superconductivity at higher temperatures - without applying high pressure - is an active area of materials research.
To make the boron-doped Q-carbon, the researchers coat a substrate with a mixture of amorphous carbon and boron. The mixture is then hit with a single laser pulse lasting for only a few nanoseconds. During this pulse, the temperature of the carbon is raised to 4,000 Kelvin and then rapidly quenched.
“By incorporating boron into the Q-carbon we eliminate the material’s ferromagnetic properties and give it superconductive properties," Narayan says. “So far, every time we have increased the amount of boron, the temperature at which the material retains its superconductive properties has increased.
“This process increases the density of carrier states near the Fermi level," relative to boron-doped diamond, Narayan says.
“The materials advance here is that this process allows a boron concentration in a carbon material that is far higher than would be possible using existing equilibrium methods, such as chemical vapor deposition," Narayan says. “Using equilibrium methods, you can only incorporate boron into Q-carbon to 2 atomic percent - two out of every 100 atoms. Using our laser-based, non-equilibrium process, we’ve reached levels as high as 27 atomic percent."
That higher concentration of boron is what gives the material its superconductivity characteristics at a higher temperature.
“Oak Ridge National Laboratory has confirmed our findings about higher density of states using electron energy loss spectroscopy," Narayan says.
“We plan to optimize the material to increase the temperature at which it is superconductive," Narayan says. “This breakthrough in high-temperature superconductivity of Q-carbon is scientifically exciting with a path to room temperature superconductivity in novel strongly bonded, light-mass materials. The superconductivity in Q-carbon has special significance for practical applications, as it is transparent, superhard and tough, biocompatible, erosion and corrosion resistant. Nothing like that exists today.
“There are already closed-cycle helium refrigeration systems designed for use with superconductors that can achieve temperatures easily as low as 10K," Narayan says. “B-doped Q-carbon can handle as much as 43 million amperes per square centimeter at 21K in the presence of a two Tesla magnetic field. Since we have demonstrated superconductivity at 57K, this means the doped Q-carbon is already viable for applications."
The most recent paper, “A Novel High-Temperature Carbon-Based Superconductor: B-Doped Q-Carbon," is published in the Journal of Applied Physics. An earlier paper, “High-Temperature Superconductivity in Boron-doped Q-Carbon," is published in the journal ACS Nano. Lead author of both papers is Anagh Bhaumik, a Ph.D. student at NC State. Both papers were co-authored by Ritesh Sachan, a National Research Council postdoctoral researcher at NC State who also works for the Army Research Office.
The research was done with support from the National Science Foundation under grant number DMR-1560838. NC State has filed for a U.S. patent for this technology.
Figure Caption: (a) High-resolution SEM shows microstructure of boron-doped Q-carbon; and (b) Magnetic moment as a function of temperature showing magnetic flux expulsion below Tc (Meissner Effect) with inset M-H loop.
Figure Caption: Temperature-dependent (normalized) resistivity measurements of B-doped Q-carbon thin films showing the onset temperature of superconducting transition temperature at 37.8 K. The inset depicts the enlarged view of the superconducting transition showing the transition width to be 1.5 K.
Other Recent News
- Researchers Find Simpler Way to Deposit Magnetic Iron Oxide onto Gold Nanorods 12.12.2017
- Researchers Inadvertently Boost Surface Area of Nickel Nanoparticles for Catalysis 11.28.2017
- Narayan to serve on NAI Fellows Advisory Committee 10.9.2017
- Nurturing the nanotech maker in us all 9.19.2017
- MSE Wins Multiple Awards and Provides Leadership at Microscopy and Microanalysis 2017 8.14.2017
- High-Temperature Superconductivity in B-doped Q-Carbon 7.24.2017
- IRES Students Gain Research experience in Denmark 7.21.2017
- MSE Graduate Student Wins MRS Poster Award 5.23.2017
- ‘Persistent Photoconductivity’ Offers New Tool for Bioelectronics 5.3.2017
- Eman Alhajji accepted into NAE Grand Challenge Scholars Program 5.2.2017